Pink Sheets 319.0 F 级铝合金——性能与标准全解
通用性能
| 性能 | 数值 | 状态 |
|---|---|---|
| 密度 | 3.0 g/cm³ | F |
机械性能
| 性能 | 数值 | 状态 | 相关标准 | 形态 | 备注 |
|---|---|---|---|---|---|
| 抗压屈服强度 | 131 MPa | F | |||
| 弹性模量 | 74 GPa | F | |||
| 弹性模量 | 78.0 GPa | F | |||
| 伸长率 | 1.5 % | F | Pink Sheets, ASTM B26, ASTM B618 | 铸件 | A100 |
| 伸长率 | 2 % | F | 砂型铸造，50 mm 标距 | ||
| 伸长率 | 2.1 % | F | |||
| 伸长率 | 2.5 % | F | Pink Sheets, ASTM B108 | 铸件 | A100 |
| 疲劳强度 | 70.0 - 83.0 MPa | F | 5×10⁸ 次循环，R.R. Moore 型试验 | ||
| 布氏硬度 | 70.0 - 85.0 | F | 500 kg 荷载，10 mm 球压头 | ||
| 布氏硬度 | 70.0 | F | Pink Sheets, ASTM B26, ASTM B618 | 铸件 | |
| 布氏硬度 | 95.0 | F | Pink Sheets, ASTM B108 | 铸件 | |
| 泊松比 | 0.33 | F | |||
| 剪切模量 | 28.0 GPa | F | |||
| 剪切强度 | 152 MPa | F | |||
| 抗拉强度 | 150.0 MPa | F | |||
| 抗拉强度 | 160.0 MPa | F | Pink Sheets, ASTM B26, ASTM B618 | 铸件 | |
| 抗拉强度 | 185.0 MPa | F | Pink Sheets, ASTM B108 | 铸件 | |
| 抗拉强度 | 186 MPa | F | 砂型铸造 | ||
| 屈服强度 (RP02) | 90.0 MPa | F | Pink Sheets, ASTM B26, ASTM B618 | 铸件 | RP02 |
| 屈服强度 (RP02) | 95.0 MPa | F | Pink Sheets, ASTM B108 | 铸件 | RP02 |
| 屈服强度 | 110.0 MPa | F | |||
| 屈服强度 (RP02) | 124 MPa | F | 砂型铸造，RP02 |
热学性能
| 性能 | 数值 | 状态 | 相关标准 | 形态 |
|---|---|---|---|---|
| 热膨胀系数 | 2.3×10⁻⁵ 1/K | F | ||
| 熔点范围 | 510.0 - 607.0 °C | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
| 熔点 | 540.0 °C | F | ||
| 比热容 | 860.0 J/(kg·K) | F | ||
| 热导率 | 110.0 W/(m·K) | F |
电学性能
| 性能 | 数值 | 状态 | 备注 |
|---|---|---|---|
| 电导率 | 16,000,000 S/m | F | 典型/推导值 |
| 电阻率 | 6.39×10⁻⁸ Ω·m | F | 典型值 |
| 相对电导率 (IACS) | 27.0 - 28.0 % | F | 典型值 |
化学成分
| 元素 | 含量范围 | 状态 | 相关标准 | 形态 |
|---|---|---|---|---|
| 铝 (Al) | 85.8 - 91.5 % | F | ||
| 铜 (Cu) | 3.0 - 4.0 % | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
| 铁 (Fe) | 1.0 % | F | ||
| 铁 (Fe) | 1.00 % | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
| 镁 (Mg) | 0.1 % | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
| 锰 (Mn) | 0.5 % | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
| 镍 (Ni) | 0.35 % | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
| 其他 | 0.5 % | F | ||
| 硅 (Si) | 5.5 - 6.5 % | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
| 钛 (Ti) | 0.25 % | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
| 锌 (Zn) | 1.0 % | F | Pink Sheets, ASTM B108, ASTM B26, ASTM B618 | 铸件 |
金属
- EN 573-3 3.0515 O3 铝合金：关键力学与热学性能
- EN 573-3 AW-4043A O3 4000系列铝合金线材规格
- EN 573-3 AW-4047A O3 高硅铝合金线材规格
- Pink Sheets 242.0 O 铝合金 — 材料性能与标准规范全解析
- EN 573-3 AW-5556A F – 高性能 5000 系列铝合金
- EN 573-3 认证 AW-5556A O3 铝合金牌号
- EN 573-3 AW-5087 F态铝合金：关键性能与标准
- AW-5087 O3态铝合金：EN 573-3认证性能参数
- Pink Sheets 319.0 T5 合金 —— 综合力学性能详解
- AW-1110F 铝材等级——EN 573-3 合规性与性能参数
- Pink Sheets 201.0 T7 铸造铝合金——高性能力学性能详解
- T61 态 Pink Sheets 242.0 铸造铝合金——详细力学性能数据