AA 5154 H36 铝合金 - 规格标准与性能详解
性能概览
一般性能
| 属性 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 密度 | 2.66 g/cm³ | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
力学性能
| 属性 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|
| 弯曲疲劳强度 | 140.0 MPa | H36 | AA 标准 | |
| 弹性模量 | 70.0 GPa | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | |
| 布氏硬度 | 78.0 | H36 | AA 标准 | |
| 平面应变断裂韧性 | 22.0 - 35.0 MPa·√m | 锻造 5000 系列铝合金典型值 | ||
| 泊松比 | 0.33 | 锻造 5000 系列铝合金典型值 | ||
| 剪切模量 | 26.0 - 26.5 GPa | 锻造 5000 系列铝合金典型值 | ||
| 抗拉强度 | 290.0 - 340.0 MPa | H36 | AA 标准, ASTM B209, ASTM B313, ASTM B547 | |
| 抗拉强度 | 290.0 MPa | H36 | AA 标准, ASTM B211 | |
| 抗拉强度 | 310.0 MPa | H36 | AA 标准, ASTM B210 |
热学性能
| 属性 | 温度 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|---|
| 热膨胀系数 | 20 °C | 2.39×10⁻⁵ 1/K | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | |
| 热膨胀系数 | 100 °C | 2.39×10⁻⁵ 1/K | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | |
| 最高使用温度 | 150.0 °C | 锻造 5000 系列铝合金典型值 | |||
| 熔点 | 590.0 - 645.0 °C | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 | ||
| 比热容 | 879.0 - 963.0 J/(kg·K) | 锻造 5000 系列铝合金典型值 | |||
| 热导率 | 126 W/(m·K) | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
电学性能
| 属性 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 电导率 | 19,000,000 S/m | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
| 电阻率 | 5.26×10⁻⁸ Ω·m | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
化学成分
| 元素 | 含量范围 | 状态 | 相关标准 |
|---|---|---|---|
| 铬 (Cr) | 0.15 - 0.35 % | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
| 铜 (Cu) | 0.1 % | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
| 铁 (Fe) | 0.40 % | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
| 镁 (Mg) | 3.1 - 3.9 % | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
| 锰 (Mn) | 0.1 % | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
| 硅 (Si) | 0.25 % | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
| 钛 (Ti) | 0.2 % | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
| 锌 (Zn) | 0.2 % | H36 | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B547 |
工艺性能
| 属性 | 评价 | |
|---|---|---|
| 钎焊 | 一般：暂无已知或开发的钎焊工艺 | |
| 耐腐蚀性 | 应力腐蚀开裂：运行和实验室测试中均无损伤；一般腐蚀：极好，在工业或海水大气中无需防护 | |
| 一般加工性 | 一般：差（O, H32），足够（H34, H36, H38） | |
| 成形性能 | 一般（状态）：良好（O），可接受（H32, H34），差（H36, H38） | |
金属
- ASTM B241 5154-O 牌号 – 优质 5000 系列铝合金
- ASTM B211 5154 H36 铝合金 —— 技术规格与性能详表
- ASTM B210 5154-O 铝合金：退火态 5000 系列无缝管规格与性能
- AA 5154 H111 铝合金：标准性能规格与应用指南
- AA 5154 H26 铝合金 – 关键力学性能与规格
- AA 5154 H28 铝合金 – ASTM B209 标准与关键力学性能
- AA 5456 O 态铝合金 – 高镁 5000 系列变形铝关键性能
- AA 5154 H22 铝合金：5xxx系列标准、力学性能与关键规格
- AA标准 5154 H24 铝合金：5xxx系列性能参数与规格详解
- AA 5083-O铝合金标准：高强度与耐腐蚀性
- AA 6066 T6 铝镁硅铜合金 – 高强度结构挤压材规范
- AA 6351 T6 铝合金 – 技术标准与性能参数