AA 5154 H112 铝标准 - 综合性能概览
一般性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 密度 | 2.66 g/cm³ | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
力学性能
| 性能 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|
| 弯曲疲劳强度 | 115.0 MPa | H112 | AA Standards | |
| 弹性模量 | 70.0 GPa | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 | |
| 布氏硬度 | 63.0 | H112 | AA Standards | |
| 平面应变断裂韧性 | 22.0 - 35.0 MPa·√m | 锻造 5000 系列铝典型值 | ||
| 泊松比 | 0.33 | 锻造 5000 系列铝典型值 | ||
| 剪切模量 | 26.0 - 26.5 GPa | 锻造 5000 系列铝典型值 | ||
| 抗拉强度 | 205.0 MPa | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 | |
| 210.0 MPa | H112 | AA Standards, ASTM B209 | ||
| 220.0 MPa | H112 | AA Standards, ASTM B209 | ||
| 240.0 MPa | H112 | AA Standards |
热学性能
| 性能 | 温度 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|---|
| 热膨胀系数 | 20 °C | 2.3899999999999998e-05 1/K | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 | |
| 100 °C | 2.3899999999999998e-05 1/K | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 | ||
| 最高使用温度 | 150.0 °C | 锻造 5000 系列铝典型值 | |||
| 熔点 | 590.0 - 645.0 °C | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 | ||
| 比热容 | 879.0 - 963.0 J/(kg·K) | 锻造 5000 系列铝典型值 | |||
| 导热系数 | 126 W/(m·K) | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
电学性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 电导率 | 19000000.0 S/m | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
| 电阻率 | 5.26e-08 Ω·m | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
化学成分
| 元素 | 含量 | 状态 | 相关标准 |
|---|---|---|---|
| 铬 | 0.15 - 0.35 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
| 铜 | 0.1 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
| 铁 | 0.40 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
| 镁 | 3.1 - 3.9 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
| 锰 | 0.1 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
| 硅 | 0.25 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
| 钛 | 0.2 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
| 锌 | 0.2 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B221 |
工艺性能
| 性能 | 描述 |
|---|---|
| 钎焊 | 一般：无已知或开发的钎焊工艺 |
| 耐腐蚀性能 | 应力腐蚀开裂：运行和实验室测试中无损伤；总体：极好，在工业或海水大气中无需防护 |
| 一般加工性 | 一般：差 (O, H32)，尚可 (H34, H36, H38) |
| 成形性 | 一般 (状态)：好 (O)，可接受 (H32, H34)，差 (H36, H38) |
金属
- ASTM B241 5154-O 牌号 – 优质 5000 系列铝合金
- ASTM B241 5154-H112 牌号 – 变形铝合金规格
- ASTM B211 5154-H112 铝合金：5xxx 系列优质棒线材规范
- ASTM B210 5154-O 铝合金：退火态 5000 系列无缝管规格与性能
- AA 5154 H111 铝合金：标准性能规格与应用指南
- AA 5154 H26 铝合金 – 关键力学性能与规格
- AA 5154 H28 铝合金 – ASTM B209 标准与关键力学性能
- AA 1060 H112 铝合金标准 — 关键性能与 ASTM 规范
- AA 3004 H112 铝合金：关键性能与性能概览
- AA 5456 O 态铝合金 – 高镁 5000 系列变形铝关键性能
- AA标准 5050 H112 铝合金：中等强度防锈铝材料性能与数据
- AA 5154 H22 铝合金：5xxx系列标准、力学性能与关键规格