AA 6061-T6 (T62) 铝合金：高强度、耐腐蚀材料规格
概述
AA 6061 是一种广泛应用的铝合金，具有良好的表面光洁度，易于阳极氧化处理。该合金焊接性和钎焊性优异，表面处理后光洁度高。它对海水和大气腐蚀具有优异的抵抗力，且适合热锻造加工。
性能参数
一般性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 密度 | 2.7 g/cm³ | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
力学性能
| 性能 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|
| 弹性模量 | 69.0 GPa | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 平面应变断裂韧性 | 22.0 - 35.0 MPa·√m | 典型锻造 6000 系列铝合金数值 | ||
| 泊松比 | 0.33 | 典型锻造 6000 系列铝合金数值 | ||
| 剪切模量 | 26.0 - 26.5 GPa | 典型锻造 6000 系列铝合金数值 | ||
| 抗拉强度 | 260.0 MPa | T62 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
| 抗拉强度 | 275.0 MPa | T62 | AA Standards, ASTM B209 | |
| 抗拉强度 | 290.0 MPa | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B483 |
热学性能
| 性能 | 温度 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|---|
| 热膨胀系数 | 20 °C | 2.36e-05 1/K | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 热膨胀系数 | 100 °C | 2.36e-05 1/K | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 熔点 | 580.0 - 650.0 °C | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
| 比热容 | 887.0 - 963.0 J/(kg·K) | 典型锻造 6000 系列铝合金数值 | |||
| 热导率 | 155.0 - 180.0 W/(m·K) | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
电学性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 电导率 | 23,000,000 - 27,000,000 S/m | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 电阻率 | 3.7e-08 - 4.35e-08 Ω·m | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
化学成分
| 元素 | 含量范围 | 状态 | 相关标准 |
|---|---|---|---|
| 铬 | 0.04 - 0.35 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 铜 | 0.15 - 0.4 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 铁 | 0.70 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 镁 | 0.8 - 1.2 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 锰 | 0.15 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 硅 | 0.4 - 0.8 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 钛 | 0.15 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 锌 | 0.25 % | T62 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
工艺性能
| 性能 | 评价 | |
|---|---|---|
| 钎焊 | 常规工艺可行 | |
| 耐腐蚀性 | 应力腐蚀开裂：运行和实验室测试均无损伤 (O, T6, T651, T652, T6510, T6511)；运行无损伤，实验室测试有限损伤 (T4, T451, T4510, T4511)；总体：良好，工业或海水大气中无需防护 | |
| 一般切削加工性 | 一般：差 (O)，尚可 (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) | |
| 成形性 | 一般 (状态)：良好 (O)，可接受 (T4, T451, T4510, T4511)，差 (T6, T651, T652, T6510, T6511) | |
金属
- ASTM B210 6061-T6/T62 铝合金：高强度、耐腐蚀、阳极氧化首选
- AA 6463 T62 铝合金：关键力学性能与规格参数
- AA 6066-T6 铝合金（T62 状态）—— 标准、力学性能与综合数据表
- AA 6061 H13 铝合金：高强度、耐腐蚀、易焊接
- ASTM B483 6061-T6/T62 铝合金：高强度、耐腐蚀结构材
- ASTM B211 6061 T6/T62/T651 铝合金：高强度、耐腐蚀、多功能材料
- AA 5456 O 态铝合金 – 高镁 5000 系列变形铝关键性能
- AA 5083-O铝合金标准：高强度与耐腐蚀性
- AA 6066 T6 铝镁硅铜合金 – 高强度结构挤压材规范
- AA 6351 T6 铝合金 – 技术标准与性能参数
- AA 6061 T89 合金—— 优质耐腐蚀、易加工的铝合金
- AA 6061 T94 铝合金 – 高性能 6061 牌号，T94 处理状态