AA 3003 O 态铝合金——高耐蚀、良好加工与焊接性能
AA 3003 铝合金是一种广受欢迎的合金，具有极佳的大气耐腐蚀性和中等强度。在铝合金中，其加工性能良好，但不可热处理强化。与其他铝合金不同，AA 3003 可采用常规焊接方法焊接。它既适应冷加工也适应热加工，其力学性能普遍优于 1000 系列铝合金。
性能参数
一般性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 密度 | 2.73 g/cm³ | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
力学性能
| 性能 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|
| 弯曲疲劳强度 | 50.0 MPa | O | AA 标准 | |
| 弹性模量 | 69.0 GPa | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |
| 布氏硬度 | 28.0 | O | AA 标准 | |
| 平面应变断裂韧性 | 22.0 - 35.0 MPa·√m | 典型锻造 3000 系列铝合金数值 | ||
| 泊松比 | 0.33 | 典型锻造 3000 系列铝合金数值 | ||
| 剪切模量 | 25.0 - 26.0 GPa | 典型锻造 3000 系列铝合金数值 | ||
| 抗拉强度 | 95.0 - 130.0 MPa | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | |
| 抗拉强度 | 95.0 MPa | O | AA 标准, ASTM B210, ASTM B483 | |
| 抗拉强度 | 110.0 MPa | O | AA 标准 | |
| 抗拉强度 | 130.0 - 135.0 MPa | O | AA 标准, ASTM B316 |
热学性能
| 性能 | 温度 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|---|
| 热膨胀系数 | 20 °C | 2.32×10⁻⁵ 1/K | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |
| 热膨胀系数 | 100 °C | 2.32×10⁻⁵ 1/K | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | |
| 熔点 | 640.0 - 655.0 °C | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 | ||
| 比热容 | 893.0 - 920.0 J/(kg·K) | 典型锻造 3000 系列铝合金数值 | |||
| 热导率 | 159.0 - 193.0 W/(m·K) | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
电学性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 电导率 | 24,000,000 - 29,000,000 S/m | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
| 电阻率 | 3.45×10⁻⁸ - 4.17×10⁻⁸ Ω·m | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
化学成分
| 元素 | 含量 | 状态 | 相关标准 |
|---|---|---|---|
| 铜 | 0.05 - 0.2 % | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
| 铁 | 0.70 % | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
| 锰 | 1.0 - 1.5 % | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
| 硅 | 0.6 % | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
| 锌 | 0.1 % | O | AA 标准, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483, ASTM B547 |
工艺性能
| 项目 | 描述 | |
|---|---|---|
| 钎焊 | 一般：可采用商业化工艺和方法 | |
| 耐腐蚀性能 | 应力腐蚀开裂：运行和实验室测试均无损伤；总体：极好，工业或海洋大气中无需防护 | |
| 一般加工性 | 一般：O、H12 状态不适用；H14、H16、H25 状态差 | |
| 成形性 | 一般（状态）：O、H12 良好；H14、H25 可接受；H16、H18 差 | |
金属
- ASTM B316 3003-H14 铝合金：优异耐腐蚀与中等强度的工业用材
- ASTM B211 3003 H12铝合金 - 耐腐蚀、可焊接、高强度
- ASTM B211 3003 H14 铝合金：耐腐蚀、可焊接、高强度合金
- ASTM B211 3003 H16 铝合金：优异耐腐蚀与高强度
- ASTM B211 3003 H18 铝合金：卓越耐腐蚀与高强度
- ASTM B316 3003O 铝合金：高耐腐蚀性与易焊接
- ASTM B483 3003-H12 铝合金管 —— 优异耐腐蚀性与焊接性
- ASTM B211 3003 H112 铝合金：卓越的耐腐蚀性与加工性能
- ASTM B234M 3003 H25 铝合金无缝管：高耐腐蚀与优异焊接性能
- ASTM B210 3003 铝合金无缝管：高强度耐腐蚀管道材料
- ASTM B210 3003-O 铝合金：软态、极佳成形性与焊接性
- ASTM B483 3003-O 铝合金 - 优异的耐腐蚀性和可焊性