AA 7178 T6 高强度镁铜铝合金 —— 先进金属加工首选
AA 7178 以铜和镁为主要合金元素，提供无妥协的高强度，适配机加工、焊接、热处理等多种金属成形工艺，是航空航天、高端装备制造的优选材料。
基本性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 密度 | 2.83 g/cm³ | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
力学性能
| 性能 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|
| 弹性模量 | 72.0 GPa | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | — |
| 平面应变断裂韧性 | 22.0–35.0 MPa·√m | — | — | 典型锻造 7000 系列铝合金值 |
| 泊松比 | 0.33 | — | — | 典型锻造 7000 系列铝合金值 |
| 剪切模量 | 26.4–27.1 GPa | — | — | 典型锻造 7000 系列铝合金值 |
| 抗拉强度 | 565.0 MPa | T6 | AA 标准, ASTM B221, ASTM B241 | — |
| 抗拉强度 | 570.0 MPa | T6 | AA 标准, ASTM B209 | — |
| 抗拉强度 | 580.0 MPa | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | — |
| 抗拉强度 | 595.0 MPa | T6 | AA 标准, ASTM B221 | — |
| 抗拉强度 | 600.0 MPa | T6 | AA 标准, ASTM B221, ASTM B241 | — |
| 抗拉强度 | 605.0 MPa | T6 | AA 标准 | — |
热学性能
| 性能 | 温度 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|---|
| 热膨胀系数 | 20 °C | 2.34×10⁻⁵ 1/K | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | — |
| 热膨胀系数 | 100 °C | 2.34×10⁻⁵ 1/K | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | — |
| 熔点范围 | — | 475.0–630.0 °C | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | — |
| 比热容 | — | 795.0–1050.0 J/(kg·K) | — | — | 典型锻造 7000 系列铝合金值 |
| 热导率 | — | 126 W/(m·K) | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 | — |
电学性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 电导率 | 18,000,000 S/m | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
| 电阻率 | 5.56×10⁻⁸ Ω·m | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
化学成分 (wt%)
| 元素 | 含量 | 状态 | 相关标准 |
|---|---|---|---|
| 铬 | 0.18–0.28% | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
| 铜 | 1.6–2.4% | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
| 铁 | 0.50% | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
| 镁 | 2.4–3.1% | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
| 锰 | 0.3% | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
| 硅 | 0.4% | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
| 钛 | 0.2% | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
| 锌 | 6.3–7.3% | T6 | AA 标准, ASTM B209, ASTM B221, ASTM B241, ASTM B316 |
工艺性能
| 项目 | 评价 |
|---|---|
| 钎焊 | 一般：无已知或开发的钎焊工艺 |
| 耐腐蚀性 | 应力腐蚀开裂：拉应力横向晶粒区域有作业损伤，实验室样品有限损伤；一般：良好，工业或海水大气中无防护亦可 |
| 通用加工性 | 一般：良好至可接受 |
| 成形加工性 | 一般(状态)：不适合 |
金属
- AA 5456 O 态铝合金 – 高镁 5000 系列变形铝关键性能
- AA 5083-O铝合金标准：高强度与耐腐蚀性
- AA 6066 T6 铝镁硅铜合金 – 高强度结构挤压材规范
- AA 6351 T6 铝合金 – 技术标准与性能参数
- AA 标准 5454 O 态铝合金 – 全面规格参数
- AA 标准 1060 O 铝合金 – 纯铝完整材料规格与标准
- AA 3004 O 态铝合金：综合性能与性能概览
- AA 5050O 铝合金 - 标准与力学性能
- AA 标准 5154-O 铝合金：关键力学性能与规格
- AA 6063 T4 铝合金——耐腐蚀性优异的优质建筑型材合金
- AA 6061-T1 铝合金：耐腐蚀、可焊接的优质材料
- AA 2219 铝合金 O 态：高强度、耐热结构级材料