AA 5052-O 铝合金：卓越的耐腐蚀性与焊接性能
AA 5052 是一种非热处理强化铝合金，具有优异的表面处理质量。与大多数铝合金相比，AA 5052 具有更好的耐腐蚀性，特别是对海水和海洋大气环境。该合金可采用大多数常见技术轻松焊接，实际上具有所有铝合金中最好的焊接特性之一。
一般性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 密度 | 2.68 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
力学性能
| 性能 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|
| 弯曲疲劳强度 | 110.0 MPa | O | AA Standards | |
| 弹性模量 | 70.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 布氏硬度 | 47.0 | O | AA Standards | |
| 平面应变断裂韧性 | 22.0 - 35.0 MPa·√m | 典型锻造 5000 系列铝合金 | ||
| 泊松比 | 0.33 | 典型锻造 5000 系列铝合金 | ||
| 剪切模量 | 26.0 - 26.5 GPa | 典型锻造 5000 系列铝合金 | ||
| 抗拉强度 | 170.0 - 215.0 MPa | O | AA Standards, ASTM B209, ASTM B313, ASTM B547 | |
| 抗拉强度 | 170.0 - 240.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241 | |
| 抗拉强度 | 170.0 - 220.0 MPa | O | AA Standards, ASTM B211 | |
| 抗拉强度 | 170.0 MPa | O | AA Standards, ASTM B483 | |
| 抗拉强度 | 195.0 MPa | O | AA Standards | |
| 抗拉强度 | 220.0 MPa | O | AA Standards, ASTM B316 |
热学性能
| 性能 | 温度 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|---|
| 热膨胀系数 | 20 °C | 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 热膨胀系数 | 100 °C | 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 最高使用温度 | 150.0 °C | 典型锻造 5000 系列铝合金 | |||
| 熔点 | 605.0 - 650.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
| 比热容 | 879.0 - 963.0 J/(kg·K) | 典型锻造 5000 系列铝合金 | |||
| 热导率 | 138 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
电学性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 电导率 | 20000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 电阻率 | 5e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
化学成分
| 元素 | 含量范围 | 状态 | 相关标准 |
|---|---|---|---|
| 铬 | 0.15 - 0.35 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 铜 | 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 铁 | 0.40 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 镁 | 2.2 - 2.8 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 锰 | 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 硅 | 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 锌 | 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
工艺性能
| 性能 | 评价 |
|---|---|
| 钎焊 | 总体：有限钎焊 |
| 耐腐蚀性 | 应力腐蚀开裂：运行和实验室测试中无损伤；总体：极好，在工业或海水大气中无需防护 |
| 一般切削加工性 | 总体：差 (O, H32)，尚可 (H34, H36, H38) |
| 成形性 | 总体 (状态)：良好 (O)，可接受 (H32, H34)，差 (H36, H38) |
金属
- AA 5456 O 态铝合金 – 高镁 5000 系列变形铝关键性能
- AA 5083-O铝合金标准：高强度与耐腐蚀性
- AA 6066 T6 铝镁硅铜合金 – 高强度结构挤压材规范
- AA 6351 T6 铝合金 – 技术标准与性能参数
- AA 标准 5454 O 态铝合金 – 全面规格参数
- AA 标准 1060 O 铝合金 – 纯铝完整材料规格与标准
- AA 3004 O 态铝合金：综合性能与性能概览
- AA 5050O 铝合金 - 标准与力学性能
- AA 标准 5154-O 铝合金：关键力学性能与规格
- AA 7178 T6 高强度镁铜铝合金 —— 先进金属加工首选
- AA 6063 T4 铝合金——耐腐蚀性优异的优质建筑型材合金
- AA 5052 H28 铝合金：卓越耐腐蚀性与焊接性能