AA 5086 铝合金：高强度、耐腐蚀的结构用铝合金
合金概述
AA 5086 是一种结构用铝合金，具有优异的耐腐蚀性能和高导电率。其强度高于 5052 和 5083 合金，且能通过应变硬化和冷加工进一步提高强度，同时保持高性价比。该合金可采用常规方法焊接，其中电弧焊为首选工艺。
物理性能
一般性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 密度 | 2.66 g/cm³ | O (退火态) | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
力学性能
| 性能 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|
| 弹性模量 | 71.0 GPa | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | |
| 平面应变断裂韧性 | 22.0 - 35.0 MPa·√m | - | - | 典型锻造 5000 系列铝合金值 |
| 泊松比 | 0.33 | - | - | 典型锻造 5000 系列铝合金值 |
| 剪切模量 | 26.0 - 26.5 GPa | - | - | 典型锻造 5000 系列铝合金值 |
| 抗拉强度 | 240.0 - 305.0 MPa | O | AA 标准, ASTM B209, ASTM B313, ASTM B547 | |
| 抗拉强度 | 240.0 - 315.0 MPa | O | AA 标准, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | |
| 抗拉强度 | 260.0 MPa | O | AA 标准 |
热学性能
| 性能 | 温度 | 数值 | 状态 | 相关标准 | 备注 |
|---|---|---|---|---|---|
| 热膨胀系数 | 20 °C | 2.38×10⁻⁵ 1/K | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | |
| 100 °C | 2.38×10⁻⁵ 1/K | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | ||
| 最高使用温度 | - | 150.0 °C | - | - | 典型锻造 5000 系列铝合金值 |
| 熔点 | - | 585.0 - 640.0 °C | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 | |
| 比热容 | - | 879.0 - 963.0 J/(kg·K) | - | - | 典型锻造 5000 系列铝合金值 |
| 导热系数 | - | 126 W/(m·K) | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
电学性能
| 性能 | 数值 | 状态 | 相关标准 |
|---|---|---|---|
| 电导率 | 18.0 MS/m | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
| 电阻率 | 5.56 ×10⁻⁸ Ω·m | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
化学成分 (质量分数, %)
| 元素 | 含量范围 | 状态 | 相关标准 |
|---|---|---|---|
| 铬 (Cr) | 0.05 - 0.25 | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
| 铜 (Cu) | 0.10 | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
| 铁 (Fe) | 0.50 | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
| 镁 (Mg) | 3.5 - 4.5 | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
| 锰 (Mn) | 0.2 - 0.7 | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
| 硅 (Si) | 0.40 | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
| 钛 (Ti) | 0.15 | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
| 锌 (Zn) | 0.25 | O | AA 标准, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547 |
工艺性能
| 性能 | 评价 | |
|---|---|---|
| 钎焊 | 一般：暂无已知或开发的钎焊工艺 | |
| 耐腐蚀性能 | 应力腐蚀开裂：运行和实验室测试均无损伤 (O, H32, H116, H111)；运行无损伤，实验室测试有限损伤 (H34, H36, H38)；总体：非常好，工业或海洋大气中无需防护 | |
| 一般加工性 | 一般：差 (O, H32, H116, H111)；尚可 (H34, H36, H38) | |
| 成形性 | 一般 (状态)：良好 (O)；可接受 (H32, H116, H111)；差 (H36, H38) | |
应用领域
AA 5086 广泛用于船舶制造、海洋工程、储罐、压力容器、汽车零部件、建筑结构件等要求高耐腐蚀性和中高强度的领域。其优异的焊接性能使其成为焊接结构件的首选材料，特别是在海洋环境下表现出色。
金属
- ASTM B210 5086-O 铝合金：高强度、耐腐蚀、高性价比退火态材料
- AA 5456 O 态铝合金 – 高镁 5000 系列变形铝关键性能
- AA 5083-O铝合金标准：高强度与耐腐蚀性
- AA 6066 T6 铝镁硅铜合金 – 高强度结构挤压材规范
- AA 6351 T6 铝合金 – 技术标准与性能参数
- AA 标准 5454 O 态铝合金 – 全面规格参数
- AA 标准 1060 O 铝合金 – 纯铝完整材料规格与标准
- AA 3004 O 态铝合金：综合性能与性能概览
- AA 5050O 铝合金 - 标准与力学性能
- AA 标准 5154-O 铝合金：关键力学性能与规格
- AA 7178 T6 高强度镁铜铝合金 —— 先进金属加工首选
- AA 6063 T4 铝合金——耐腐蚀性优异的优质建筑型材合金