EN 10217-2 X12CrMo91 调质钢 — 加氢容器用优质高温钢
X12CrMo91 调质钢适用于高压加氢容器。退火态下耐高压氢气及侵蚀性油品；调质态下亦用于容器及装置制造。典型应用：水合装置、石油蒸馏装置管材。
性能参数
一般性能
| 属性 | 温度 | 数值 |
|---|---|---|
| 密度 | 20.0 °C | 7.77 g/cm³ |
力学性能
| 属性 | 温度 | 数值 |
|---|---|---|
| 弹性模量 | 20.0 °C | 211.67 – 218 GPa |
| 95.0 °C | 208.22 GPa | |
| 100.0 °C | 213 – 214 GPa | |
| 150.0 °C | 204.77 GPa | |
| 200.0 °C | 206 – 207 GPa | |
| 205.0 °C | 200.64 GPa | |
| 260.0 °C | 196.5 GPa | |
| 300.0 °C | 198 – 199 GPa | |
| 315.0 °C | 191.67 GPa | |
| 370.0 °C | 186.85 GPa | |
| 400.0 °C | 190 GPa | |
| 425.0 °C | 181.33 GPa | |
| 485.0 °C | 175.82 GPa | |
| 500.0 °C | 180 GPa | |
| 540.0 °C | 170.3 GPa | |
| 595.0 °C | 165.47 GPa | |
| 600.0 °C | 167 – 168 GPa | |
| 650.0 °C | 159.96 GPa | |
| 700.0 °C | 150 GPa | |
| 760.0 °C | 137.21 GPa | |
| 伸长率 | 20.0 °C | 20 % |
| 横向伸长率 | 20.0 °C | 18 % |
| 泊松比 | 20.0 °C | 0.30 |
| 95.0 °C | 0.30 | |
| 150.0 °C | 0.30 | |
| 205.0 °C | 0.30 | |
| 260.0 °C | 0.30 | |
| 315.0 °C | 0.30 | |
| 370.0 °C | 0.30 | |
| 425.0 °C | 0.30 | |
| 485.0 °C | 0.31 | |
| 540.0 °C | 0.31 | |
| 595.0 °C | 0.30 | |
| 650.0 °C | 0.33 | |
| 760.0 °C | 0.33 | |
| 剪切模量 | 20.0 °C | 81.7 GPa |
| 95.0 °C | 80.32 GPa | |
| 150.0 °C | 78.95 GPa | |
| 205.0 °C | 77.22 GPa | |
| 260.0 °C | 75.5 GPa | |
| 315.0 °C | 73.77 GPa | |
| 370.0 °C | 71.71 GPa | |
| 425.0 °C | 69.64 GPa | |
| 485.0 °C | 67.22 GPa | |
| 540.0 °C | 65.16 GPa | |
| 595.0 °C | 63.43 GPa | |
| 650.0 °C | 60.33 GPa | |
| 760.0 °C | 51.71 GPa | |
| 抗拉强度 | 20.0 °C | 590 – 740 MPa |
| 100.0 °C | 550 MPa | |
| 150.0 °C | 525 MPa | |
| 200.0 °C | 500 MPa | |
| 250.0 °C | 490 MPa | |
| 300.0 °C | 480 MPa | |
| 350.0 °C | 460 MPa | |
| 400.0 °C | 430 MPa | |
| 450.0 °C | 405 MPa | |
| 500.0 °C | 360 MPa | |
| 横向抗拉强度 | 20.0 °C | 590 – 740 MPa |
| 屈服强度 Rp0.2 | 20.0 °C | 390 MPa |
| 100.0 °C | 375 MPa | |
| 150.0 °C | 365 MPa | |
| 200.0 °C | 355 MPa | |
| 250.0 °C | 345 MPa | |
| 300.0 °C | 335 MPa | |
| 350.0 °C | 325 MPa | |
| 400.0 °C | 315 MPa | |
| 450.0 °C | 295 MPa | |
| 500.0 °C | 275 MPa | |
| 横向屈服强度 Rp0.2 | 20.0 °C | 390 MPa |
热学性能
| 属性 | 温度 | 数值 | 备注 |
|---|---|---|---|
| 热膨胀系数 | -100.0 °C | 1.00E-5 1/K | |
| 20.0 °C | 1.08E-5 1/K | ||
| 100.0 °C | 1.12E-5 – 1.13E-5 1/K | ||
| 200.0 °C | 1.16E-5 – 1.18E-5 1/K | ||
| 300.0 °C | 1.20E-5 – 1.23E-5 1/K | ||
| 400.0 °C | 1.23E-5 – 1.27E-5 1/K | ||
| 425.0 °C | 1.19E-5 1/K | ||
| 485.0 °C | 1.22E-5 1/K | ||
| 500.0 °C | 1.26E-5 – 1.30E-5 1/K | ||
| 540.0 °C | 1.23E-5 1/K | ||
| 595.0 °C | 1.25E-5 1/K | ||
| 600.0 °C | 1.29E-5 – 1.32E-5 1/K | ||
| 650.0 °C | 1.27E-5 1/K | ||
| 700.0 °C | 1.33E-5 1/K | ||
| 熔点 | — | 1382 – 1529 °C | 铬钼钢典型值 |
| 比热容 | 20.0 °C | 429 J/(kg·K) | |
| 100.0 °C | 464 – 500 J/(kg·K) | ||
| 200.0 °C | 492 – 530 J/(kg·K) | ||
| 300.0 °C | 511 – 560 J/(kg·K) | ||
| 400.0 °C | 531 – 610 J/(kg·K) | ||
| 500.0 °C | 554 – 680 J/(kg·K) | ||
| 600.0 °C | 585 – 780 J/(kg·K) | ||
| 700.0 °C | 626 J/(kg·K) | ||
| 导热系数 | 20.0 °C | 20.7 W/(m·K) | |
| 100.0 °C | 22.6 – 23.0 W/(m·K) | ||
| 200.0 °C | 24.0 – 24.4 W/(m·K) | ||
| 300.0 °C | 25.8 – 26.0 W/(m·K) | ||
| 400.0 °C | 26.9 – 27.0 W/(m·K) | ||
| 500.0 °C | 27.8 – 28.0 W/(m·K) | ||
| 600.0 °C | 28.5 – 29.0 W/(m·K) | ||
| 700.0 °C | 28.8 W/(m·K) | ||
| 热扩散率 | 20.0 °C | 6.2 mm²/s | |
| 100.0 °C | 5.9 mm²/s | ||
| 200.0 °C | 6.0 mm²/s | ||
| 300.0 °C | 6.0 mm²/s | ||
| 400.0 °C | 5.7 mm²/s | ||
| 500.0 °C | 5.4 mm²/s | ||
| 600.0 °C | 4.8 mm²/s | ||
| 700.0 °C | 4.0 mm²/s |
电学性能
| 属性 | 温度 | 数值 |
|---|---|---|
| 电阻率 | 20.0 °C | 5.03E-7 Ω·m |
| 100.0 °C | 5.67E-7 – 5.70E-7 Ω·m | |
| 200.0 °C | 6.47E-7 – 6.50E-7 Ω·m | |
| 300.0 °C | 7.27E-7 – 7.30E-7 Ω·m | |
| 400.0 °C | 8.09E-7 – 8.10E-7 Ω·m | |
| 500.0 °C | 8.90E-7 Ω·m | |
| 600.0 °C | 9.70E-7 – 9.72E-7 Ω·m | |
| 700.0 °C | 1.06E-6 Ω·m |
化学成分
| 元素 | 含量 |
|---|---|
| 碳 | 0.15 % |
| 铬 | 8 – 10 % |
| 锰 | 0.3 – 0.6 % |
| 钼 | 0.9 – 1.1 % |
| 磷 | 0.03 % |
| 硅 | 0.25 – 1.0 % |
| 硫 | 0.03 % |
金属
- EN 10137-2 S890QL 级 – 重载应用高强度淬火回火钢
- EN 10137-3 S500A级：用于结构应用的淬火回火细晶粒钢
- EN 10083-1 51CrV4 调质钢 (QT) – 全温域性能数据手册
- EN 10213 G17CrMo9-10 淬火回火钢——高温高压应用
- EN 10085 15CrMoV5.9 钢 - 调质钢，用于耐磨机械零件
- EN 10085 31CrMo12 钢——重载工况用高性能调质钢
- EN 10216-2 11CrMo9-10无缝钢管：高温高压用淬火回火钢管性能
- EN 10132-3 42CrMo4 调质合金钢：优质冷轧带钢性能详解
- EN 10089 60Cr3 调质钢：弹簧与机械应用的理想选择
- EN 10273 13CrMo4-5 调质钢 – 高温性能卓越
- EN 10222-4 P420QH 淬火回火钢 - 高强度可焊压力容器用钢
- EN 10213 G17CrMo5-5 调质钢：汽轮机与锅炉壳体的高性能铸钢